ASTM F136-13 or ASTM B348-13, Ti-6Al-4V Grade 23 ELI, extra low oxygen content, 0.25â€³ (6.35 mm) diameter wire, annealed to allow for easy uncoiling. Each spool to be produced with a maximum of 3 weld joints. The wire will have a bright and clean surface.
In general, the wire must contain a very low level of interstitial elements, especially oxygen. The aluminum concentration range specified is relatively high, to compensate for potential aluminum loss to the process.
Wire and coiling requirements are critical as the wire will be uncoiled, straightened and fed to a Plasma
Wire and coiling requirements are critical as the wire will be uncoiled, straightened and fed to a Plasma Atomization reactor.
Up to three welding joints
Welding joints within the tolerance of wire diameter
Coil weight (range): 50 to 60 kg
Free of residual stress
Properly coiled for easy unwinding (see Figure 1)
Coil inner diameter (ID): between 500-1150 mm
Coil maximum outer diameter (OD): < 1500 mm
Coil maximum height (h): < 250 mm
Diameter and tolerance (inches) 0.250â€³ +/- 0.002â€³
Diameter and tolerance (millimeters) 6.35 mm +/- 0.05 mm
Vacuum annealed for easy straightening.
Polished (clean and free of contaminants)
We will provide customer a proper Mill Test Certificate before shipping, containing at minimum the elemental chemical analysis for Al, V, Fe, C, N, H, O, Ti, and the result of visual and dimensional inspection. The wire must be checked for surface contamination and tested for mechanical properties. China 3D Printer Wire manufacturers
website:www.aati-cathode.com/3d-printer-wire/More details: China 3D Printer Wire Manufacturers